A Nanocomposite Sol-Gel Film Based on PbS Quantum Dots Embedded into an Amorphous Host Inorganic Matrix.

In this study, a sol-gel film based on lead sulfide (PbS) quantum dots incorporated into a host network was synthesized as a special nanostructured composite material with potential applications in temperature sensor systems. This work dealt with the optical, structural, and morphological properties of a representative PbS quantum dot (QD)-containing thin film belonging to the Al2O3-SiO2-P2O5 system. The film was prepared using the sol-gel method combined with the spin coating technique, starting from a precursor solution containing a suspension of PbS QDs in toluene with a narrow size distribution and coated on a glass substrate in a multilayer process, followed by annealing of each deposited layer. The size (approximately 10 nm) of the lead sulfide nanocrystallites was validated by XRD and by the quantum confinement effect based on the band gap value and by TEM results. The photoluminescence peak of 1505 nm was very close to that of the precursor PbS QD solution, which demonstrated that the synthesis route of the film preserved the optical emission characteristic of the PbS QDs. The photoluminescence of the lead sulfide QD-containing film in the near infrared domain demonstrates that this material is a promising candidate for future sensing applications in temperature monitoring.

Effect of P2O5 Content on Luminescence of Reduced Graphene-Oxide-Doped ZnO-P2O5 Nano-Structured Films Prepared via the Sol-Gel Method.

A convenient and low-cost sol-gel approach for the one-step synthesis of ZnO-P2O5-rGO nanostructures with tuned bandgap and fluorescence was investigated. The obtained hybrid nanostructures exploit the properties of zinc oxide, graphene oxide and phosphorous oxide as promising candidates for a wide range of optoelectronic applications. A predominant amorphous structure, ZnO-P2O5-rGO, containing ZnO nanorods was evidenced by X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM). The estimated size of the ZnO nanorods in nanostructures with P2O5 was noticed to decrease when the P2O5/ZnO ratio was increased. The presence of ZnO, P2O5 and rGO was confirmed by Fourier-transform infrared spectroscopy (FTIR) and Raman investigation. P2O5 was noticed to tune the bandgap and the fluorescence emissions of the nanostructured films, as estimated by UV-Vis-NIR and fluorescence spectroscopy, respectively. The electrical measurements performed at room temperature showed that the main influence on the film's resistivity does not come from the 1% rGO doping but from the P2O5/ZnO ratio. It was found that a 10/90 molar ratio of P2O5/ZnO decreases the resistivity almost seven-fold compared with rGO-doped ZnO films.

Nanostructured PbS-Doped Inorganic Film Synthesized by Sol-Gel Route.

IV-VI semiconductor quantum dots embedded into an inorganic matrix represent nanostructured composite materials with potential application in temperature sensor systems. This study explores the optical, structural, and morphological properties of a novel PbS quantum dots (QDs)-doped inorganic thin film belonging to the Al2O3-SiO2-P2O5 system. The film was synthesized by the sol-gel method, spin coating technique, starting from a precursor solution deposited on a glass substrate in a multilayer process, followed by drying of each deposited layer. Crystalline PbS QDs embedded in the inorganic vitreous host matrix formed a nanocomposite material. Specific investigations such as X-ray diffraction (XRD), optical absorbance in the ultraviolet (UV)-visible (Vis)-near infrared (NIR) domain, NIR luminescence, Raman spectroscopy, scanning electron microscopy-energy dispersive X-ray (SEM-EDX), and atomic force microscopy (AFM) were used to obtain a comprehensive characterization of the deposited film. The dimensions of the PbS nanocrystallite phase were corroborated by XRD, SEM-EDX, and AFM results. The luminescence band from 1400 nm follows the luminescence peak of the precursor solution and that of the dopant solution. The emission of the PbS-doped film in the NIR domain is a premise for potential application in temperature sensing systems.

Investigations Regarding the Addition of ZnO and Li2O-TiO2 to Phosphate-Tellurite Glasses: Structural, Chemical, and Mechanical Properties.

Phosphate and tellurite glasses can be used in optics, optoelectronics, magneto-optics, and nuclear and medical fields. Two series of phosphate-tellurite glasses, (50-x)ZnO-10Al2O3-40P2O5-xTeO2 and (40-x)Li2O-10Al2O3-5TiO2-45P2O5-xTeO2 (x = 5, 10), were synthesized by a non-conventional wet-route, and the mechanical properties as key performance measures for their application in optoelectronics were investigated. X-ray Diffraction (XRD) measurements revealed the vitreous nature of the investigated materials. Instrumented indentation tests allowed the calculation of hardness (H) and Young's modulus (E) using the Oliver and Pharr model. The influence of increasing the TeO2 content, as well as the substitution of ZnO by Li2O-TiO2, on the variation of hardness, Young's modulus, penetration depth (PD), and fracture toughness (FT) was evaluated in both series. As a general trend, there is a decrease in the hardness and Young's modulus with increasing penetration depth. The addition of Li2O and TiO2 instead of ZnO leads to improved hardness and elastic modulus values. Regarding the H/E ratio, it was found that the samples with lower TeO2 content should be significantly more crack-resistant compared to the higher TeO2 content samples. The H3/E2 ratio, being lower than 0.01, revealed a poor resistance of these glasses to plastic deformation. At the same time, a decrease of the fracture toughness with increasing TeO2 content was noticed for each glass series. Based on dilatometry measurements, the thermal expansion coefficient as well as the characteristic temperatures of the glasses were measured. Field Emission Scanning Electron Microscopy-Energy Dispersive X-ray analysis (FESEM-EDX) revealed a uniform distribution of the elements in the bulk samples. The mechanical properties of these vitreous materials are important in relation to their application as magneto-optical Faraday rotators in laser cavities.

A New Zinc Phosphate-Tellurite Glass for Magneto-Optical Applications.

This work investigates the structural, magnetic and magneto-optical properties of a new zinc phosphate-tellurite glass belonging to the 45ZnO-10Al2O3-40P2O5-5TeO2 system. The glass was prepared by a wet method of processing the starting reagents followed by suitable melting-stirring-quenching-annealing steps. Specific parameters such as density, average molecular mass, molar volume, oxygen packaging density, refractive index, molar refractivity, electronic polarizability, reflection loss, optical transmission, band gap and optical basicity have been reported together with thermal, magnetic and magneto-optical characteristics. Absorption bands appear in the blue and red visible region, while over 600 nm the glass becomes more transparent. FTIR and Raman spectra evidenced phosphate-tellurite vibration modes proving the P2O5 and TeO2 network forming role. Magnetic measurements reveal the diamagnetic character of the Te-doped glass with an additional weak ferromagnetic signal, specific to diluted ferromagnetic oxides. Positive Faraday rotation angle with monotonous decreasing value at increasing wavelength was evidenced from magneto-optical measurements. The final product is a composite material comprising of a non-crystalline vitreous phase and Te-based nanoclusters accompanied by oxygen vacancies. The metallic-like Te colloids are responsible for the dark reddish color of the glass whereas the accompanying oxygen vacancies might be responsible for the weak ferromagnetic signal persisting up to room temperature.